@article{ref1,
title="The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline by theoretical simulations and experimental measurements",
journal="Corrosion reviews",
year="2021",
author="Zhao, Bo and Zhao, Zhijuan and Jin, Dong and Li, Na and Liu, Linlin and Cao, Xin and Shou, Binan",
volume="39",
number="6",
pages="573-587",
abstract="The corrosion behavior and cracking susceptibility of the disbonded coating in the X80 steel pipeline were investigated by different methods. The oxygen content in the trapped solution decreased rapidly with the formation of an airtight disbonded area. The airtight system affected the electrode reaction process, resulting in the inhibition of corrosion in the center of the disbonded area and the more refined surface finish of the sample. The bottom of the disbonded area underwent a relatively intense and accelerated corrosion reaction controlled by the diffusion process. The cracking susceptibility of the X80 steel firstly decreased and then increased in the pointing direction. © 2021 Walter de Gruyter  Keywords: Pipeline transportation <p /> <p>Language: en</p>",
language="en",
issn="0334-6005",
doi="10.1515/corrrev-2021-0013",
url="http://dx.doi.org/10.1515/corrrev-2021-0013"
}