@article{ref1,
title="Correlation between defect depth and defect length through a reliability index when evaluating of the remaining life of steel pipeline under corrosion and crack defects",
journal="Engineering failure analysis",
year="2017",
author="Zelmati, Djamel and Ghelloudj, Oualid and Amirat, Abdelaziz",
volume="79",
number="",
pages="171-185",
abstract="Despite the various engineering models existing for lifetime investigation of hydrocarbon steel pipelines under localized corrosion and crack defects there is still a lack of information about the correlation between the two main parameters characterizing the geometrical defect model, depth and length. So the aim of the present work is a contribution in evaluating the remaining life of the pipeline using reliability analysis in order to correlate the two parameters through one common parameter, the reliability index. As a first step, the investigation is carried out on four standard and well established engineering models; Irwin, SINTAP, ASME B31G and Modified ASME B31G methods, aiming to coordinate results given by each of the four models. The potential defect depth and length correlation through a reliability index can be used as a decision-making tool to give realistic answers for replacing and/or repairing a tube subjected to internal pressure and on which flaws of different depths and lengths have been detected from inspection of a pipeline after few years of service.   Keywords: Pipeline transportation<p /> <p>Language: en</p>",
language="en",
issn="1350-6307",
doi="10.1016/j.engfailanal.2017.04.025",
url="http://dx.doi.org/10.1016/j.engfailanal.2017.04.025"
}