TY - JOUR PY - 1999// TI - Measurements of the effects of smoke on active circuits JO - Fire and materials A1 - Tanaka, TJ SP - 103 EP - 108 VL - 23 IS - 3 N2 - Smoke has long been recognized as the most common source of fire damage to electrical equipment; however, most failures have been analysed after the fire was out and the smoke vented. The effects caused while the smoke is still in the air have not been explored. Such effects have implications for new digital equipment being installed in nuclear reactors. The US Nuclear Regulatory Commission is sponsoring work to determine the impact of smoke on digital instrumentation and control. As part of this programme, Sandia National Laboratories has tested simple active circuits to determine how smoke affects them. These tests included the study of three possible failure modes on a functional board: (1) circuit bridging, (2) corrosion (metal loss), and (3) induction of stray capacitance. The performance of nine different circuits was measured continuously on bare and conformally coated boards during smoke exposures lasting 1 h each and continued for 24 h after the exposure started, The circuit that was most affected by smoke (100% change in measured values) was the one most sensitive to circuit bridging. Its high impedance (50 M Omega) was shorted during the exposure, but in some cases recovered after the smoke was vented, The other two failure modes, corrosion and induced stray capacitance, caused little change in the function of the circuits. The smoke permanently increased resistance, of the circuit tested for corrosion, implying that the contacts were corroded. However, the change was very small (less than 2%). The stray-capacitance test circuit showed very little change after a smoke exposure in either the short or long term. The results of the tests suggest that conformal coatings and type of circuit are major considerations when designing digital circuitry to be used in critical control systems.

LA - SN - 0308-0501 UR - http://dx.doi.org/ ID - ref1 ER -